French Vanilla Opalescent
Fusible, 2mm, Stained Glass
Cold Characteristics
Uniform color.
Working Notes
This sulfur-bearing glass may react with gold-bearing lead (001311, 001215) and copper (001116, 001408, 001417, 000144, 000145, 000146) glasses to create dark interface (lead sulfide, copper sulfide).
Very viscous; will flow later and less than other glasses. Generally more sensitive to heat-history and more likely to show variation in color after fusing than many opals. When fired on edge, a clear distinction between outside and interior surfaces is commonly seen (a variation used by designers). This glass may become increasingly white with repeated firings. Consider using glass from the same batch for a given project.
Dense White (000313) Reaction Note: The fired surface of French Vanilla does not react as readily to lead-bearing Dense White (000313), compared to firing the same combination in a single firing (using glass that has not previously been fired).
Bullseye Compatible.
Fusible / Bullseye-compatible. Matching COEs does not ensure compatibility between glasses from Bullseye and another manufacturer. All compatible Bullseye glasses are tested compatible with other Bullseye compatible glass.
Photo above is a general representation of glass colors. Colors may vary. Sizes are Approximate.
Possible Applications:
- Mosaic Projects
- Stained Glass Projects
- Fusing - 90 COE
Striker
This style may not reveal (strike to) its target color until fired.
Reactive Potential
Contains: Sulfur (S) / Selenium (Se)
May React With: Copper (Cu), Lead (Pb), and Silver (Ag)